JSW Neosteel EDS TMT bars are high-strength Fe 550D grade rebars engineered with enhanced ductility. Their unique chemistry and post-rolling treatment enable maximum energy absorption, helping structures withstand severe earthquake shocks. This critical flexibility allows the bars to bend without fracturing, offering superior safety and resilience in seismic zones.
Verified for use in earthquake resistant structures due to high ductility and energy absorption capacity.
Fe 550D grade high-strength steel engineered to deliver enhanced protection during powerful earthquakes.
Best-in-class rib pattern with a high AR value that bonds best with cement.
HYQST technology ensures a uniform quality, visible as concentric rings in the bar’s cross-section.
High-grade steel with ultra-low sulphur and phosphorus for maximum strength and lasting durability.
The inherent microstructure, featuring a soft ferrite and pearlite core, ensures easy bendability.
| Mechanical Properties | IS 1786:2008 for Fe 550D | JSW Neosteel Fe 550D | IS 13920:2016* | JSW Neosteel EDS 550D | Chemical Properties | IS 1786:2008 for Fe 550D | JSW Neosteel Fe 550D | IS 13920:2016* | JSW Neosteel EDS 550D |
|---|---|---|---|---|---|---|---|---|---|
| YS (Mpa) (Min) | 550 | 570 | 550 | 570 | % C (Max) | 570 | 0.24 | 0.25 | 0.23 |
| UTS (Mpa) (Min) | 600 | 630 | 600 | 670 | % P (Max) | 670 | 0.04 | 0.25 | 0.25 |
| UTS/YS (Min) | 1.08 | 1.12 | 1.15 | 1.15-1.18% | % S (Max) | 1.15-1.18% | 0.04 | 1.15 | 0.03 |
| %EL (Min) | 14.5 | 16 | 14.5 | 16%-18% | CE (Max) | 16%-18% | 0.07 | 14.5 | 0.5 |
| Total %EL at Max force | 5 | 7 | 5 | 7 | % S+P (Max) | 7 | 0.012 | 0.012 | 0.06 |
| Dia (mm) | 8-25mm | 8-25mm | Nitrogen (ppm) | 8-25mm | 0.5 | 0.61 | 1.00 |